COR-TEN is suitable for flame cutting provided proper operating methods are used. At temperatures below 5°C a sufficiently wide zone on either side of the intended cut should be preheated. If flame cut edges are to undergo cold forming, the hardening effect should be prevented by preheating - as in the case of S355J2 or the hardened zones must be worked off e.g. by appropriate grinding.