Fe-360C Steel Chemical Composition,Fe-360C Steel Mechanical Properties

Bebon steel can supply Fe-360C Steel Chemical Composition,Fe-360C Steel Mechanical Properties price and specification ,we are steel suppliers and manufacturer,you can contact us to get Fe-360C Steel Chemical Composition,Fe-360C Steel Mechanical Properties application and other informations.

Fe-360C steel is a structural billet steel for structural applications. Fe-360C is a material grade and designation defined in ISO 630 standard. ISO 630 is an international material standard for billet steel for general structural usage. Fe-360C Steel is similar to Fe-360B steel except minor tolerances in chemical composition.

Fe-360C Steel Dimensional Characteristics : The applicable thickness for this Fe-360C material as defined in the ISO 630 starts from 10 mm to 200 mm.

Fe-360C Steel Chemical Composition : ISO 630 defines the chemical composition of Fe-360C steels as under:

Maximum percentage of Carbon (C) is 0.17.

Maximum percentage of Manganese (Mn) is 1.4.

Maximum percentage of Phosphorous (P) is 0.040.

Maximum percentage of Sulphur (S) is 0.040.

Maximum percentage of Silicon (Si) is 0.40.

Remaining is iron (Fe) percentage and with few negligible impurities.

Fe-360C Steel Mechanical Properties : The tensile strength of the Fe-360C Steels is expressed in Newton per millimeters and it must be at-least 340 N/mm2 (MPa) and maximum can be 470 N/mm2 (MPa). The yield strength is minimum 235 N/mm2 (MPa) for less than 16 mm, 225 N/mm2 (MPa) for 16 mm to 40 mm, 215 N/mm2 (MPa) for 40mm to 60mm and 185 N/mm2 for 150mm to 200mm. The minimum percentage ranges for elongation is 21% thicknesses.

Billets are also used for manufacturing of hot rolled steel. SPHC steel is a most common example of hot rolled steel.